- Детали
-
Објавено: Вторник, 29 Март 2016 09:21
-
Напишано од Bodal
Category: Products for plastic deformation processing - sheet metal deep drawing
ISO-L-MHE
SRPS B.H3.526
FAM IS 04 101
Inactive oil of mineral base. It is used for the lubrication in the operation of deep drawing of sheets (d < 2 mm), made of steel, light and non-ferrous metals in manufacturing of simple configuration blanks in metalworking industry and in production of domestic technical appliances. It is removed from blanks by water solution of industrial washing products and it is also possible with organic solvents.
| Viscosity at 40 ºC (mm²/s) |
100 |
| Density at 20 ºC (g/mL) |
0.930 |
| Flash point (ºC) |
min 190 |
| Packing |
180kg |
- Детали
-
Објавено: Вторник, 29 Март 2016 09:19
-
Напишано од Bodal
Category: Products for plastic deformation processing - sheet metal deep drawing
ISO-L-MHE
SRPS B.H3.526
FAM IS 04 102
Inactive oils of mineral base. They are used for the lubrication in the operation of deep drawing of sheets (d > 2 mm), made of steel, light and non-ferrous metals in manufacturing of complex configuration blanks in automobile industry and in production of domestic technical appliances. They are used in concentrate form and they can also be used as pseudo-emulsion with water (water is gradually added to oil while stirring intensively).
| Viscosity at 40 ºC (mm²/s) |
170 140 |
| Density at 20 ºC (g/mL) |
0.950 |
| Flash point (ºC) |
min 180 |
| Packing |
20kg 180kg |
- Детали
-
Објавено: Вторник, 29 Март 2016 09:18
-
Напишано од Bodal
Category: Products for plastic deformation processing - sheet metal deep drawing
ISO-L-MHE
SRPS B.H3.526
FAM IS 04 102
Inactive oil of mineral base. It is used for the lubrication in the operation of deep drawing of sheets (d > 2 mm), made of steel, light and non-ferrous metals in manufacturing of complex configuration blanks in automobile industry and in production of domestic technical appliances. It is used in concentrate form and it can also be used as pseudo-emulsion with water (water is gradually added to oil while stirring intensively).
| Viscosity at 40 ºC (mm²/s) |
140 |
| Density at 20 ºC (g/mL) |
0.920 |
| Flash point (ºC) |
min 180 |
| Packing |
180kg |
- Детали
-
Објавено: Вторник, 29 Март 2016 09:17
-
Напишано од Bodal
Category: Products for plastic deformation processing - sheet metal deep drawing
ISO-L-MAI
SRPS B.H3.526
FAM IS 04 102
Lubricant made from animal fats. It is used for the lubrication in complex deep drawing operations and drawing down of steel sheets in metalworking industry and domestic technical appliances production industry. It is used in concentrate form and also as pseudo-emulsion with water in the ratio of 1:1 to 1:20 (water is gradually added into lubricant while stirring intensively). It is removed from blanks by water solution of industrial washing products and it is also possible with organic solvents.
| Viscosity at 40 ºC (mm²/s) |
330 |
| Density at 20 ºC (g/mL) |
- |
| Flash point (ºC) |
min 180 |
| Packing |
180kg |
- Детали
-
Објавено: Вторник, 29 Март 2016 09:16
-
Напишано од Bodal
Category: Products for plastic deformation processing - sheet metal deep drawing
ISO-L-MHB
FAM IS 04 107
Product for cooling and lubrication of tools used for silicon sheet metal punching of electric engines and transformators. It spreads well on the surface and it has mild odour.
| Vaporation rate at 20ºC (ether=1) |
15 |
| Density at 20 ºC (g/mL) |
0.800 |
| Flash point (ºC) |
min 18 |
| Packing |
17kg 160kg |